ATA International Product Catalogue

306486 306486 1439 Material group Strength N/mm 2  2  3  4  5  6  8  10  12 1.1-1.2-1.3-1.4-1.5 Unalloyed stells <1100 N/mm 2 ap ae n vf 0.04 0.10 38,000 7,500 0.06 0.15 25,500 7,000 0.08 0.20 19,000 6,500 0.10 0.25 16,000 6,000 0.12 0.30 12,000 7,500 0.16 0.40 9,000 6,500 0.20 0.50 7,000 6,000 0.24 0.60 6,000 5,500 2.1-2.2-2.3-2.4-2.5- 2.6 Alloy steels <30 HRC ap ae n vf 0.04 0.10 38,000 7,500 0.06 0.15 25,500 7,000 0.08 0.20 19,000 6,500 0.10 0.25 16,000 6,000 0.12 0.30 12,000 7,000 0.16 0.40 9,000 6,000 0.20 0.50 7,000 5,000 0.24 0.60 6,000 5,000 3.1-3.2 High alloy steels <35 HRC ap ae n vf 0.04 0.10 28,000 7,000 0.06 0.15 28,000 6,700 0.08 0.20 24,000 6,000 0.10 0.25 12,000 5,800 0.12 0.30 9,000 5,500 0.16 0.40 7,000 5,000 0.20 0.50 5,500 4,500 0.24 0.60 4,500 4,000 4.1-4.2-4.3 Stainless steels <45 HRC ap ae n vf 0.04 0.10 26,000 4,500 0.06 0.15 17,000 4,500 0.08 0.20 13,000 4,000 0.10 0.25 11,000 3,800 0.12 0.30 8,500 5,000 0.16 0.40 6,500 4,500 0.20 0.50 5,000 4,000 0.24 0.60 4,000 3,500 8.1 Hardened steels <55 HRC a ae n vf 0.04 0.10 22,000 3,200 0.06 0.15 15,000 3,100 0.08 0.20 11,000 3,000 0.10 0.25 9,000 3,000 0.12 0.30 7,000 3,500 0.16 0.40 5,200 3,200 0.20 0.50 4,000 2,600 0.24 0.60 3,500 2,400 8.2 Hardened Steels <60 HRC ap ae n vf 0.04 0.10 17,000 2,700 0.06 0.15 11,500 2,500 0.08 0.20 8,500 2,200 0.10 0.25 7,200 2,000 0.12 0.30 6,500 3,000 0.16 0.40 5,000 2,800 0.20 0.50 4,000 2,500 0.24 0.60 3,200 2,200 8.3 Hardened steels <65 HRC ap ae n vf 0.04 0.10 14,000 2,300 0.06 0.15 9,000 2,200 0.08 0.20 7,000 2,000 0.10 0.25 5,500 1,900 0.12 0.30 5,800 2,500 0.16 0.40 4,200 2,200 0.20 0.50 3,500 2,000 0.24 0.60 2,800 1,500 8.3 Hardened steels <70 HRC ap ae n vf 0.04 0.10 8,500 1,400 0.06 0.15 5,500 1,300 0.08 0.20 4,400 1,200 0.10 0.25 3,500 1,100 0.12 0.30 3,700 1,500 0.16 0.40 2,800 1,300 0.20 0.50 2,200 1,200 0.24 0.60 1,800 1,000 Material group Strength N/mm 2  2  3  4  5  6  8  10  12 1.1-1.2-1.3-1.4-1.5 Unalloyed stells <1100 N/mm 2 ap ae n vf 0.04 0.10 55,000 10,000 0.06 0.15 35,000 9,500 0.08 0.20 27,000 9,000 0.10 0.25 22,000 8,000 0.12 0.30 18,000 11,000 0.16 0.40 13,500 10,000 0.20 0.50 11,000 9,000 0.24 0.60 9,000 8,500 2.1-2.2-2.3-2.4-2.5- 2.6 Alloy steels <30 HRC ap ae n vf 0.04 0.10 55,000 9,500 0.06 0.15 35,000 9,000 0.08 0.20 27,000 8,500 0.10 0.25 22,000 7,500 0.12 0.30 18,000 10,000 0.16 0.40 13,500 9,500 0.20 0.50 11,000 8,500 0.24 0.60 9,000 8,000 3.1-3.2 High alloy steels <35 HRC ap ae n vf 0.04 0.10 45,000 9,000 0.06 0.15 30,000 8,500 0.08 0.20 23,000 8,000 0.10 0.25 20,000 7,500 0.12 0.30 17,000 10,000 0.16 0.40 12,500 9,500 0.20 0.50 10,000 8,500 0.24 0.60 8,500 8,000 4.1-4.2-4.3 Stainless steels <45 HRC ap ae n vf 0.04 0.10 44,000 8,200 0.06 0.15 29,000 7,500 0.08 0.20 22,000 6,500 0.10 0.25 18,000 6,200 0.12 0.30 16,500 9,800 0.16 0.40 12,500 8,500 0.20 0.50 9,500 7,500 0.24 0.60 8,000 7,000 8.1 Hardened steels <55 HRC ap ae n vf 0.04 0.10 36,000 6,200 0.06 0.15 24,500 5,200 0.08 0.20 18,000 4,800 0.10 0.25 15,000 5,000 0.12 0.25 14,000 7,000 0.16 0.40 10,000 6,000 0.20 0.50 8,000 5,500 0.24 0.50 7,000 5,000 8.2 Hardened steels <60 HRC ap ae n vf 0.04 0.10 27,000 4,200 0.06 0.15 18,000 3,800 0.08 0.20 13,000 3,500 0.10 0.25 11,000 3,200 0.12 0.25 11,000 5,000 0.16 0.40 8,000 4,500 0.20 0.50 6,500 4,000 0.24 0.50 5,500 3,500 8.3 Hardened steels <65 HRC ap ae n vf 0.04 0.10 25,000 4,000 0.06 0.15 17,000 3,500 0.08 0.20 13,000 3,200 0.10 0.25 10,000 3,000 0.12 0.25 10,000 4,500 0.16 0.40 7,500 4,000 0.20 0.50 6,000 3,200 0.24 0.50 5,000 2,800 8.3 Hardened steels <70 HRC ap ae n vf 0.04 0.10 17,500 2,700 0.06 0.15 11,500 2,500 0.08 0.20 8,500 2,200 0.10 0.25 7,000 2,000 0.12 0.25 7,000 2,500 0.16 0.40 5,100 2,400 0.20 0.50 4,100 2,200 0.24 0.50 3,500 1,800 HPC -Finishing HSC -Finishing Processing information: 1. Conditions must be: ridgid machine circumstances and excellent holders. 2. Reduce the cutting data when you machine with long neck length. 3. The stated cutting date belongs to a neck length of max 4×D and a tapered workpiece of max. 15°. 4. I f the corneradius of the workpiece contour is smaler than 1.5× end mill radius or the worpiece contour ist to steep, you have to reduce the cutting data up to 50% Recommended cutting data for Karnasch solid carbide ball nose 3D – 4 flutes Recommended cutting data for Karnasch solid carbide ball nose 3D – 4 flutes 11 Index 10 9 OIL 8 7 6 5 4 3 2 1